Bioblend BT25I HH WB

biopolymer compound

injection molding

general description

- type: biopolymer compound
- main blend: mineral filler
- secondary blend: -
- degradation: in controlled conditions
- rigidity: low
- temperature stability: up to 90°C
- transparency: -
- natural color: white
- manufacturing process: injection molding

basic characteristics

biomass blend

compound base

applications

mineral

bio-based

compound color

white

degradation

home compostable

toothbrush

technical data (TDS)

density

g/cm3

MFI (190°C/2.16 kg)

g/10 min

HDT-B (@ 0.46 MPa)

°C

melting point

°C

tensile strength

MPa

tensile modulus

GPa

MPa

flexural strength

GPa

flexural modulus

elongation @ yield

elongation @ break

shore hardness

impact IZOD (notched)

J/m

material shrinkage

Test Methods: ASTM D1238, ASTM D648, ASTM D638, ASTM D790A, ASTM D638, ASTM D256, ASTM D2240; typical values; all mechanical properties as per ASTM D638 Type I specimen, injection molded in accordance with AST; D4101.